环烯烃共聚物（COC）的是一种非晶态的高分子聚合物，只有几个别制造商生产。COC是一个相对较新级别的聚合物，
COC特性：
密度小,
吸水率小,
双折射率小,
高耐热性透明树脂,
机械性优良,
耐擦伤性良好,
易密封、不透水蒸气防湿,
介电常数低，高频性能好,
易成型.
主要用于：光学镜头、光学播音器、多边镜、角摸板用保护膜、液晶显示屏用导光板、光学半导体、光纤和分析化学仪器用池和槽。聚乙烯相比。这种材料主要用于要求玻璃般清晰产品，包括镜头，小瓶，显示器和设备。
TOPAS® 5013S-04
环烯烃共聚物
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 5013S-04 is a high flow injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. The 5013 resin series features high flow characteristics for excellent mold detail replication. Lower leachables and extractables of TOPAS COC preserve content stability and quality, and chemical purity. This grade has a high heat distortion temperature to withstand 95°C PCR protocols, and is suitable for gamma or EtO procedures.
Selected Applications
Microfluidics
Microplates and biochips
Labware
Optics
Cuvettes
Electronics
Healthcare and food contact
Leading Attributes
Exceptional mold detail replication; machinable
Heat and chemical resistant, clarity and purity
Temperature resistance, clarity and purity
Clarity, low birefringence, low moisture sensitivity
More UV transparent than most resins (see 8007X10)
Low dielectric constant, thermoplastic
Broad regulatory compliance
Related Grades for Injection Molding, Healthcare, Optics and Diagnostics
TOPAS 5013L-10 - lubricated version for greater processing versatility
TOPAS 6013S-04 - general purpose version with standard flow
TOPAS 6013M-07 - broader processing version especially suited for IBM/ISBM
TOPAS 6015S-04 - higher heat distortion temperature (150°C) for 134°C protocols
TOPAS IT X1 - impact grade for applications requiring extra toughness

环烯烃共聚物（COC）的是一种非晶态的高分子聚合物，只有几个别制造商生产。COC是一个相对较新级别的聚合物，与聚丙烯和聚乙烯相比。这种材料主要用于要求玻璃般清晰产品，包括镜头，小瓶，显示器和设备。　环烯烃共聚物的自然形态，类似玻璃。典型环烯烃共聚物材料，比高密度聚乙烯和聚丙烯模量较高。由于其化学，模量越高，就越变得脆。环烯烃共聚物也是一个防潮湿的，低吸水率的高透明聚合物。在应用领域，环烯烃共聚物是一个低萃取物纯度高的产品。环烯烃共聚物也是一个无卤素产品。

TOPAS® 6013F-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 6013M-07 Topas Advanced Polymers, Inc. COC;
TOPAS® 5013S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 5013F-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 6013S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 5013L-10 Topas Advanced Polymers, Inc. COC;
TOPAS® 6015S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007F-600 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007F-400 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007F-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 6017S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007D-61 Topas Advanced Polymers, Inc. COC;
TOPAS® 7010F-600 Topas Advanced Polymers, Inc. COC;
TOPAS® 9903D-10 Topas Advanced Polymers, Inc. COC;
TOPAS® Elastomer E-140 Topas Advanced Polymers, Inc. COC;
TOPAS® 6017S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007F-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 8007S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 6015S-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 5013L-10 Topas Advanced Polymers, Inc. COC;
TOPAS® 6013M-07 Topas Advanced Polymers, Inc. COC;
TOPAS® 6013F-04 Topas Advanced Polymers, Inc. COC;
TOPAS® 6013L-17  Co., Ltd. COC;
TOPAS® 6013EC-01  Co., Ltd. COC;
TOPAS® 8007F-500  Co., Ltd. COC;
TOPAS® 9506F-04  Co., Ltd. COC;
TOPAS® 9506F-500  Co., Ltd. COC;
TOPAS® 6013S-04  Co., Ltd. COC;
TOPAS® 9506F-500  Co., Ltd. COC;

TOPAS® 8007S-04 COC低萃取物; 共聚物; 无 BPA; 无卤; 无定形的; 清晰度，高; 环氧乙烷消毒; 纯度高; 耐化... 光学应用; /护理用品; 器械; 实验室器具; 瓶子; 电气/电子应用领域; 管件; 药品包。
TOPAS® 6013M-07 COC低萃取物; 共聚物; 无 BPA; 无卤; 无定形的; 清晰度，高; 环氧乙烷消毒; 用蒸汽消毒; ... 光学应用; /护理用品; 吹塑成型应用; 器械; 实验室器具; 瓶子; 电气/电子应用领域。
TOPAS® 5013L-10 COC 共聚物; 可切削; 无定形的; 流动性高; 润滑; 清晰度，高; 环氧乙烷消毒; 纯度高; 耐化学品... 光学应用; /护理用品; 实验室器具; 电气/电子应用领域。
TOPAS® 5013F-04 COC 共聚物; 无 BPA; 无卤; 无定形的; 流动性高; 清晰度，高; 纯度高; 耐化学品性能，良好;... 包装; 混合; 片材; 薄膜; 食品包装。
TOPAS® 5013S-04 COC 低萃取物; 共聚物; 可切削; 无定形的; 流动性高; 清晰度，高; 环氧乙烷消毒; 纯度高; 耐化... 光学应用; /护理用品; 实验室器具; 电气/电子应用领域; 非特定食品应用。
TOPAS® 6015S-04 COC 低萃取物; 共聚物; 无 BPA; 无卤; 无定形的; 清晰度，高; 热消毒; 环氧乙烷消毒; 用蒸... 光学应用; /护理用品; 器械; 实验室器具; 瓶子; 电气/电子应用领域; 管件; 药品包。
TOPAS® 6013F-04 COC 共聚物; 无 BPA; 无卤; 无定形的; 清晰度，高; 纯度高; 耐化学品性能，良好; 耐热性，高... 包装; 流延薄膜; 混合; 片材; 药品包装; 薄膜; 通用; 食品包装。
TOPAS® 6017S-04 COC 低萃取物; 共聚物; 尺寸稳定性良好; 无 BPA; 无卤; 无定形的; 清晰度，高; 热消毒; 环... 光学应用; /护理用品; 器械; 实验室器具; 瓶子; 电气/电子应用领域; 管件; 药品包装; 食品包装。
TOPAS® 8007X10 COC 共聚物; 可切削; 尺寸稳定性良好; 无 BPA; 无卤; 无定形的; 清晰度，高; 纯度高; 耐化... 光学应用; /护理用品; 非特定食品应用。
TOPAS® 8007F-600 COC 中等透明度; 共聚物; 收缩性高; 无 BPA; 无卤; 无定形的; 纯度高; 耐化学品性能，良好;... 包装; 多层薄膜; 标签; 流延薄膜; 混合; 片材; 薄膜; 通用; 食品包装
耐冲击COC--COC加工成型:COC可用成型、吹塑挤出成型，中空成型，压延成型等多种方式加工。COC易吸湿，因此成型前
一定要严格进行干燥处理，一般是在110度的温度下，对材料干燥4-6小时左右。这样有利于改善制品外观。如果采用注塑成型在对制品冷却阶段要快速冷却，这样有利于增加制品的透明度，但要注易制品开裂现象。COC在注塑成型时，料简后部温度一般为
240度至270度左右中部温一般为250至310度之间刺篇后部温度为260度至310度左右。注嘴温度在250度至310
之间。模具温度应为110至145度左右，COC理想加工温度一般在260度至310之间。注塑压力在50MPa至110MPa。速度一般选中等偏快。保压压力一般在30到60MPa之间。COC挤出成型时选用单螺杆机，若用双螺杆机一定要保证有足够的压力和加热。特别是大件制品，若温度太低，压力不足，COC大件制品易开裂。